Mo-B-C and Ta-B-C Nanostructured Layers with Promising Fracture Toughness

Varování

Publikace nespadá pod Pedagogickou fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.

Autoři	BURŠÍK Jiří KUBĚNA Ivo BURŠÍKOVÁ Vilma SOUČEK Pavel ZÁBRANSKÝ Lukáš VAŠINA Petr
Rok publikování	2016
Druh	Článek ve sborníku
Konference	Defect and Diffusion Forum
Fakulta / Pracoviště MU	Přírodovědecká fakulta
Citace
Doi	http://dx.doi.org/10.4028/www.scientific.net/DDF.368.107
Obor	Fyzika plazmatu a výboje v plynech
Klíčová slova	nanolaminate; FIB; SEM; TEM; fracture toughness
Popis	X-B-C (X=Mo, Ta) layers prepared by magnetron sputtering were tested. Mechanical properties were characterized by means of nanoindentation experiments in both the static and the dynamic loading regime. The results were correlated with observations of the microstructure under indentation prints by means of scanning and transmission electron microscopy on cross sections prepared using a focussed ion beam. An excellent fracture resistance of prepared nanostructured coatings was found.
Související projekty:	Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků