Characterization of sintered Ag nanopowder joints using nanoindentation tests

Investor logo

Warning

This publication doesn't include Faculty of Education. It includes Faculty of Science. Official publication website can be found on muni.cz.
Authors

BURŠÍK Jiří SOPOUŠEK Jiří BURŠÍKOVÁ Vilma STÝSKALÍK Aleš ŠKODA David

Year of publication 2011
Type Article in Periodical
Magazine / Source Chem. listy
MU Faculty or unit

Faculty of Science

Citation
Field Plasma physics
Keywords Nanoindentation; Silver nanopowder; Solder
Description Sandwiches consisting of copper disks with Ag nanopowder interlayer annealed at various temperatures from 200 to 350 C were studied. The main emphasis was placed on the characterization of quality of the sintered Ag layers by means of nanoindentation experiments. The highest hardness values were obtained after annealing at 350 C. The highest values of the Young's modulus were achieved after annealing at 250 C, indicating the lowest porosity of the sintered layer.